Steel fiber alumina abrasive casting material/steel fiber alumina silicon carbide casting material
Specification: 25kg/bag
Steel fiber corundum silicon carbide wear-resistant casting material is made by using electric fused brown corundum and silicon carbide the main raw materials, adding heat-resistant steel fiber; the silicon carbide in corundum silicon carbide casting material has high thermal conductivity and small coefficient of expansion, and the silicon carbide is protected at high temperature. The oxidation, good oxidation resistance. Therefore, the corundum silicon carbide casting made of corundum and silicon carbide has strong wear resistance and resistance to corrosion of acidic and alkaline materials. The advantages of corundum carbide: it contains corundum raw materials, has high temperature resistance, high load softening temperature, contains explosion-proof fibers, can open the water vapor, reduce internal stress, prevent smoke cracking, and improve the service cycle. The raw material is electric fused corundum silicon carbide particles, which has high strength wear resistance and scouring resistance. Application industry: waste incineration power generation, solid waste treatment, cement rotary kiln, chemical industry and othern furnaces.
Project
| Steel fiber corundum abrasive casting material |
Al2O3/% | ≥75 |
SiC/% | 10 |
Volume density g/cm³ | 2.7 |
Heating wire variation rate/% | ±0.5 |
Pressure resistance/MPa | 90 |
Construction water addition/% | 5-6 |
Use temperature/℃ | 1500 |
Construction method | Shuttering Vibration |
Application area | Rotary kiln mouth, kiln tail, cooling machine and other abrasion-resistant parts |
Previous : Steel fiber alumina-mullite castable
Next : Cold mashed paste/coarse seam paste/anode paste
Copy product links
Long by picture save/share
INQUIRY
Add Successfully
INQUIRY
Add Successfully
HOME | About | Product | News | Case | Contact
Phone：+86 13603821221 E-mail：zzhanc@126.com
Address：河南省新密市牛店镇古角村
Copyright 2025 Huaang. All Rights Reserved
Copyright 2025 Huaang. All Rights Reserved